CALIBRATION OF THE CORROSION CRACKING MODEL OF PROTECTIVE CONCRETE LAYER
https://doi.org/10.33979/2073-7416-2021-94-2-56-62
Abstract
The article presents a method for determining the stresses arising in the protective layer of concrete in the presence of a porous zone around the "steel-concrete" interphase medium. It has been shown that radial cracks form and propagate in the concrete surrounding the reinforcement until the ultimate serviceability state, such as chipping or delamination of concrete, occurs. The generated hoop tensile stresses in concrete strongly depend on the ratio of the volume of a unit mass of rust to the volume of iron. Calculated formulas for the pressure applied by corrosion products to the concrete layer are given.
About the Authors
Ashot G. Tamrazyan
National Research Moscow State University of Civil Engineering
Russian Federation
Russian Federation
Mikhail S. Mineev
National Research Moscow State University of Civil Engineering
Russian Federation
Russian Federation
References
1. Меркулов С.И., Пахомова Е.Г., Гордеев А.В., Маяков А.С. Исследование работоспособности изгибаемых железобетонных конструкций с учетом коррозионных повреждений // Известия Курского государственного технического университета. 2009. № 4. С. 74-78
2. Смоляго Г.А., Дронов. В.И., Дронов А.В., Меркулов С.И. Изучение влияния дефектов железобетонных конструкций на развитие коррозионных процессов арматуры // Промышленное и гражданское строительство. 2014. №12. С. 49-51
3. Бондаренко В.М. О влиянии коррозионных повреждений на силовое сопротивление железобетонных конструкций // Бетон и железобетон. 1999. №6. С.27-30
4. Тамразян А.Г. К оценке риска чрезвычайных ситуаций по основным признакам его проявления на сооружение // Бетон и железобетон. 2001. № 5. С. 8-10
5. Angst U., Elsener B., Jamali A., Adey B. Concrete cover cracking owing to reinforcement corrosion - theoretical considerations and practical experience // Materials and Corrosion. 63(12). 1069-1076
6. Angst U. Chloride induced reinforcement corrosion in concrete: Concept of critical chloride content - methods and mechanisms. (Doctoral Thesis). Norwegian University of Science and Technology
7. Tamrazyan A., Popov D. Reduce of bearing strength of the bent reinforced concrete elements on a sloping section with the corrosive damage of transversal armature. В сборнике: MATEC Web of Conferences. 2017. С. 00162
8. Колчунов В.И., Меркулов С.И., Дворников В.М. Усиление железобетонных конструкций эксплуатируемых зданий и сооружений // Известия Курского государственного технического университета. 2004. № 1. С. 117-122
9. Wang X.H., Liu X.L. Modelling effects of corrosion on cover cracking and bond in reinforced concrete. Magazine of Concrete Research. 56(4). 191-199
10. Bhargava K., Ghosh A.K., Mori Y., Ramanujam S. Modeling of time to corrosion- induced cover cracking in reinforced concrete structures. Cement and Concrete Research, 35, 2203-2218
11. Тамразян А.Г., Минеев М.С. Матрица жесткости корродированных железобетонных элементов для конечно элементного моделирования. Сборник материалов XXI Международной научно-технической конференции «Актуальные проблемы строительства и строительной индустрии» (29-30 июня 2020 г.). Тула, 2020. С. 161-166
Review
For citations:
Tamrazyan A.G., Mineev M.S. CALIBRATION OF THE CORROSION CRACKING MODEL OF PROTECTIVE CONCRETE LAYER. Building and Reconstruction. 2021;(2):56-62. (In Russ.) https://doi.org/10.33979/2073-7416-2021-94-2-56-62
Views:
127
Email this article 